1、翻譯 英文原文 COMMINUTION IN A NON-CYLINDRICAL ROLL CRUSHER* P. VELLETRI ~ and D.M. WEEDON ~ ~[ Dept. of Mechanical & Materials Engineering, University of Western Australia, 35 Stirling Hwv, Crawley 6009, Australia. E-mail piero@mech.uwa.edu.au Faculty of Engineering and Physical Systems, Central Q

2、ueensland University, PO Box 1!:;19, Gladstone, Qld. 4680, Australia (Received 3 May 2001; accepted 4 September 2001) ABSTRACT Low reduction ratios and high wear rates are the two characteristics ntost commonh" associated with conventional roll crushers. Because of this, roll crushers are not of

3、ten considered Jor use in mineral processing circuits, attd many of their advantages are being largely overlooked. This paper describes a novel roll crusher that has been developed ipt order to address these issues.Relbrred to as the NCRC (Non-Cylindrical Roll Crusher), the new crusher incorporates

4、two rolls comprised qf an alternating arrangement of platte attd convex or concave su@wes. These unique roll prqfiles improve the angle qf nip, enabling the NCRC to achieve higher reduction ratios than conventional roll crushers. Tests with a model prototype have indicated thar evell fi)r very hard

5、ores, reduction ratios exceeding lO:l can be attained. In addition, since the comminution process in the NCRC combines the actions of roll arM jaw crushers there is a possibili O that the new profiles may lead to reduced roll wear rates. 2001 Elsevier Science Ltd. All rights reserved. Keywords:

6、Comminution; crushing INTRODUCTION Conventional roll crushers suffer from several disadvantages that have lcd to their lack of popularity in mineral processing applications. In particular, their low reduction ratios (typically limited to about 3:1) and high wear rates make them unattractive when c

7、ompared to other types of comminution equipment, such as cone crushers. There are, however, some characteristics of roll crushers that are very desirable from a mineral processing point of view. The relatively constant operating gap in a roll crusher gives good control over product size. The use of

8、 spring-loaded rolls make these machines tolerant to uncrushable material (such as tramp metal). In addition, roll crushers work by drawing material into the compression region between the rolls and do not rely on gravitational feeci ~like cone and jaw crushers. This generates a continuous crushing

9、cycle, which yields high throughput rates and also makes the crusher capable of processing wet and sticky ore. The NCRC is a novel roll crusher that has been dcveloped at the University of Western Australia in ordcr to address some of the problems associated with conventional roll crushers. The new

10、crusher incorporates two rolls comprised of an alternating arrangement of plane and convex or concave surfaccs. Thcse unique roll profiles improve the angle of nip, enabling the NCRC to achieve higher reduction ratios than conventional roll crushers. Preliminary tests with a model prototype have in

11、dicated that, even for very hard oics, reduction ratios exceeding 10:I can be attained (Vellelri and Weedon, 2000). These initial findings were obtained for single particle feed. where there is no significant interaction between particles during comminution. The current work extends the existing re

12、sults bv examining inulti-particle comminution inthe NCRC. It also looks at various othcr factors that influencc the perli~rmance of the NCRC and explores the effectiveness of using the NCRC for the processing of mill scats. PRINCIPLE OF OPERATION The angle of nip is one of the main lectors effcc

13、ting the performance of a roll crusher. Smaller nip angles are beneficial since they increase tl~e likelihood of parlictes bcing grabbed and crushed by lhe rolls. For a given feed size and roll gap, the nip angle in a conventional rtHl crusher is limited by the size of thc rolls. The NCRC attempt

14、s to overcome this limitation through the use of profiled rolls, which improve the angle of nip at various points during one cycle (or revolution) of the rolls. In addition to the nip angle, a number of other factors including variation m roll gap and mode of commmution were considered when select

15、ing Ille roll profiles. The final shapes of the NCRC rolls are shown in Figure I. One of the rolls consists {sI an alternating arrangement of plane and convex surfaces, while the other is formed from an alternating arrangement of phme and concave surlaccs. The shape of the rolls on the NCRC re

16、sult in several unique characteristics. Tile most important is that, lk)r a given particle size and roll gap, the nip angle generated m the NCRC will not remain constant as the rolls rotate. There will be times when the nip angle is much lower than it would be for the same sized cylindrical rolls

17、 and times when it will be much highcr. The actual variation in nip angle over a 60 degree roll rotation is illustrated in Figure 2, which also shows the nip angle generated under similar conditions m a cylindrical roll crusher of comparable size. These nip angles were calculated for a 25ram diame

18、ter circular particle between roll of approximately 200ram diameter set at a I mm minimum gap. This example can be used to illustrate the potential advantage of using non-cylindrical rolls. In order for a particle to be gripped, thc angle of nip should normally not exceed 25 . Thus, the cylindri

19、cal roll crusher would never nip this particle, since the actual nip angle remains constant at approximately 52 . The nip angle generated by the NCRC, however, tidls below 25 once as the rolls rotate by (~0 degrees. This means that the non-cylindrical rolls have a possibility of nipping the part

20、iclc 6 times during one roll rewHution. EXPERIMENTAL PROCEDURE The laboratory scale prototype of the NCRC (Figure 3) consists of two roll units, each comprising a motor, gearbox and profiled roll. Both units are mounted on linear bearings, which effectively support any vertical componcnt of forc

21、e while enabling horizontal motion. One roll unit is horizontally fixed while the other is restrained via a compression spring, which allows it to resist a varying degree of horizontal load. The pre-load on the movable roll can be adjusted up to a maximum of 20kN. The two motors that drive the

22、rolls are electronically synchronised through a variable speed controller, enabling the roll speed to be continuously varied up to 14 rpm (approximately 0.14 m/s surface speed). The rolls have a centre-to-centre distance ~,at zero gap setting) of I88mm and a width of 100mm. Both drive shafts are i

23、nstrumented with strain gauges to enable the roll torque to be measured. Additional sensors are provided to measure the horizontal force on the stationary roll and the gap between the rolls. Clear glass is fitted to the sides of the NCRC to facilitate viewing of the crushing zonc during operation

24、 and also allows the crushing sequence to bc recorded using a high-speed digital camera. Tests were performed on several types of rocks including granite, diorite, mineral ore, mill scats and concrete. The granite and diorite were obtained from separate commercial quarries; the former had been

25、 pre-crushed and sized, while the latter was as-blasted rock. The first of the ore samples was SAG mill feed obtained from Normandy Minings Golden Grove operations, while the mill scats were obtained from Aurora Golds Mt Muro mine site in central Kalimantan. The mill scats included metal particles

26、 of up to 18ram diameter from worn and broken grinding media. The concrete consisted of cylindrical samples (25mm diameter by 25ram high) that were prepared in the laboratory in accordance with the relevant Australian Standards. Unconfined uniaxial compression tests were performed on core samples

27、 (25mm diameter by 25mm high) taken from a number of the ores. The results indicated strength ranging from 60 MPa for the prepared concrete up to 260 MPa for the Golden Grove ore samples. All of the samples were initially passed through a 37.5mm sieve to remove any oversized particles. The under

28、sized ore was then sampled and sieved to determine the feed size distribution. For each trial approximately 2500g of sample was crushed in the NCRC. This sample size was chosen on the basis of statistical tests, which indicated that at least 2000g of sample needed to be crushed in order to estimat

29、e the product P80 to within +0.1ram with 95% confidence. The product was collected and riffled into ten subsamples, and a standard wet/dry sieving method was then used to determine the product size distribution. For each trial, two of the sub-samples were initially sieved. Additional sub-samples

30、were sieved if there were any significant differences in the resulting product size distributions. A number of comminution tests were conducted using the NCRC to determine the effects of various parameters including roll gap, roll force, feed size, and the effect of single and multi-particle feed

31、. The roll speed was set at maximum and was not varied between trials as previous experiments had concluded that there was little effect of roll speed on product size distribution. It should be noted that the roll gap settings quoted refer to the minimum roll gap. Due to the non-cylindrical shape

32、 of the rolls, the actual roll gap will vary up to 1.7 mm above the minimum setting (ie: a roll gap selling of l mm actually means 1-2.7mm roll gap). RESULTS Feed material The performance of all comminution equipment is dependent on the type of material being crushed. In this respect, the NCRC

33、 is no different. Softer materials crushed in the NCRC yield a lower P80 than harder materials. Figure 4 shows the product size distribution obtained when several different materials were crushed under similar conditions in the NCRC. It is interesting to note that apart from the prepared concrete

34、 samples, the P80 values obtained from the various materials were fairly consistent. These results reflect the degree of control over product size distribution that can be obtained with the NCRC. Multiple feed particles Previous trials with the NCRC were conducted using only single feed particles

35、 where there was little or no interaction between particles. Although very effective, the low throughput rates associated with this mode of comminution makes it unsuitable for practical applications. Therefore it was necessary to determine the effect that a continuous feed would have to the resul

36、ting product size distribution. In these tests, the NCRC was continuously supplied with feed to maintain a bed of material level with the top of the rolls. Figure 5 shows the effect that continuous feed to the NCRC had on the product size distribution for the Normandy Ore. These results seem to s

37、how a slight increase in P80 with continuous (multi-particle) feed, however the shift is so small as to make it statistically insignificant. Similarly, the product size distributions would seem to indicate a larger proportion of fines for the continuously fed trial, but the actual difference is ne

38、gligible. Similar trials were also conducted with the granite samples using two different roll gaps, as shown in Figure 6. Once again there was little variation between the single and multi-particle tests. Not surprisingly, the difference was even less significant at the larger roll gap, where th

39、e degree of comminution (and hence interaction between particles) is smaller. All of these tests would seem to indicate that continuous feeding has minimal effect on the performance of the NCRC. However, it is important to realise that the feed particles used in these trials were spread over a

40、 very small size range, as evident by the feed size distribution shown in Figure 6 (the feed particles in the Normandy trials were even more uniform). The unilormity in feed particle size results in a large amount of free space, which allow:s for swelling of the broken ore in the crushing chamber,

41、 thereby limiting the amount of interaction between particles. True "choke" feeding of the NCRC with ore having a wide distribution of particle sizes (especially in the smaller size range) is likely to generate much larger pressures in the crushing zone. Since the NCRC is not designed to act as a

42、 "high pressure grinding roll" a larger number of oversize particles would pass between the rolls under these circumstances. Roll gap As with a traditional roll crusher, the roll gap setting on the NCRC has a direct influence on the product size distribution and throughput of the crusher. Figu

43、re 7 shows the resulting product size distribution obtained when the Aurora Gold ore (mill scats) was crushed at three different roll gaps. Plotting the PSO values taken from this graph against the roll gap yields the linear relationship shown in Figure 8. As explained previously, the actual roll

44、 gap on the NCRC will vary over one revolution. This variation accounts for the difference between the specified gap setting and product Ps0 obtained from the crushing trials. Figure 8 also shows the effect of roll gap on throughput of the crusher and gives an indication of the crushing rates tha

45、t can be obtained with the laboratory scale model NCRC. Roll force The NCRC is designed to operate with minimal interaction between particles, such that comminution is primarily achieved by fracture of particles directly between the rolls. As a consequence, the roll force only needs to bc la

46、rge enough to overcome the combined compressive strengths of the particles between the roll surlaces. If the roll force is not large enough then the ore particles will separate the rolls allowing oversized particles to lall through. Increasing the roll force reduces the tendency of the rolls to se

47、parate and therefore provides better control over product size. However, once a limiting roll force has been reached (which is dependent on the size and type of material being crushed) any further increase in roll force adds nothing to the performance of the roll crusher. This is demonstrated in

48、Figure 9, which shows that for granite feed of 25-3 Imm size, a roll force of approximately 16 to 18 kN is required to control the product size. Using a larger roll force has little effect on the product size, although there is a rapid increase in product P80 if the roll force is reduced bek>w th

49、is level. As mentioned previously, the feed size distribution has a significant effect on the pressure generated in the crushing chamber. Ore that has a finer feed size distribution tends to "choke" the NCRC more, reducing the effectiveness of the crusher. However, as long as the pressure gener

50、ated in not excessive the NCRC maintains a relatively constant operating gap irrespective of the feed size. The product size distribution will, therefore, also bc independent of the feed size distribution. This is illustrated in Figure 10, which shows the results of two crushing trials using iden

51、tical equipment settings but with feed ore having different size distributions. In this example, the NCRC reduced the courser ore from an Fs0 of 34mm to a Ps0 of 3.0mm (reduction ratio of 11:1), while the finer ore was reduced from an Fs0 of 18mm to a Pso of 3.4mm (reduction ratio of 5:1). These

52、results suggest that the advantages of using profiled rolls diminish as the ratio of the feed size to roll size is reduced. In other words, to achieve higher reduction ratios the feed particles must be large enough to take advantage of the improved nip angles generated in the NCRC. Mill scats

53、Some grinding circuits employ a recycle or pebble crusher (such as a cone crusher) to process material which builds up in a mill and which the mill finds hard to break (mill scats). The mill scats often contain worn or broken grinding media, which can find its way into the recycle crusher. A toler

54、ance to uncrushable material is therefore a desirable characteristic for a pebble crusher to have. The NCRC seems ideally suited to such an application, since one of the rolls has the ability to yield allowing the uncrushable material to pass through. The product size distributions shown in Figu

55、re 1 1 were obtained from the processing of mill scats in the NCRC. Identical equipment settings and feed size distributions were used for both results, however one of the trials was conducted using feed ore in which the grinding media had been removed. As expected, the NCRC was able to process t

56、he feed ore containing grinding media without incident. However, since one roll was often moving in order to allow the grinding media to pass, a number of oversized particles were able to fall through the gap without being broken. Consequently, the product size distribution for this feed ore show

57、s a shift towards the larger particle sizes, and the Ps0 value increases from 4ram to 4.7mm. In spite of this, the NCRC was still able to achieve a reduction ratio of almost 4:1. Wear Although no specific tesls were conducted to determine the wear rates on the rolls of the NCRC, a number of th

58、e crushing trials were recorded using a high-speed video camera in order to try and understand the comminution mechanism. By observing particles being broken between the rolls it is possible to identify portions of the rolls which are likely to suffer from high wear and to make some subjective con

59、clusions as to the effect that this wear will have on the perlbrmance of the NCRC. Not surprisingly, the region that shows up as being the prime candidate for high wcar is the transition between the flat and concave surfaces. What is surprising is that this edge does not play a significant role i

60、n generating the improved nip angles. The performance of the NCRC should not be adversely effccted by wear to this edge because it is actually the transition between the fiat and convex surfaces (on the opposing roll) that results in the reduced nip angles. The vide() also shows that tor part of

61、 each cycle particles are comminuted between the flat surfaces of the rolls, in much the same way as they would be in a jaw crusher. This can be clearly seen on the sequence of images in Figure 12. The wear on the rolls during this part of the cycle is likely to be minimal since there is little o

62、r no relative motion between the particles and the surface of the rolls. CONCLUSIONS The results presented have demonstrated some of the factors effecting the comminution of particles in a non-cylindrical roll crusher. The high reduction ratios obtained from early single particle tests can stil

63、l be achieved with continuous multi-particle feed. However, as with a traditional roll crusher, the NCRC is susceptible to choke feeding and must be starvation fed in order to operate effectively. The type of feed material has little effect on the performance of the NCRC and, although not tested,

64、 it is anticipated that the moisture content of the feed ore will also not adversely affect the crushers per[Brmance. Results from the mill scat trials are particularly promising because they demonstrate that the NCRC is able to process ore containing metal from worn grinding media. The above fac

65、tors, in combination with the flaky nature of the product generated, indicate that the NCRC would make an excellent recycle or pebble crusher. It would also be interesting to determine whether there is any difference in the ball mill energy required to grind product obtained from the NCRC compare

66、d that obtained from a cone crusher. 中文譯文 摘要 低的破碎比和高的磨損率是與傳統(tǒng)的破碎機(jī)相聯(lián)系的很常見(jiàn)的兩個(gè)特性。因?yàn)檫@點(diǎn)，在礦石處理流程的應(yīng)用中，很少考慮到它們，并且忽略了很多它們的優(yōu)點(diǎn)。本文描述了一個(gè)已被發(fā)展起來(lái)的新穎的對(duì)輥破碎機(jī)，旨在提出這些論點(diǎn)。作為NCRC,這種新式破碎機(jī)結(jié)合了兩個(gè)輥筒，它們由一個(gè)交替布置的平面和一個(gè)凸的或者凹的表面組成。這種獨(dú)特的輥筒外形提高了嚙合角，使NCRC可以達(dá)到比傳統(tǒng)輥式破碎機(jī)更高的破碎比。用一個(gè)模型樣機(jī)做的試驗(yàn)表明：即使對(duì)于非常硬的礦石，破碎比任可以超過(guò)10。另外，既然在NCRC的破碎處理中結(jié)合了輥式和顎式破碎機(jī)的作用，那就有一種可能：那種新的輪廓會(huì)帶來(lái)輥?zhàn)幽p率的降低。 關(guān)鍵字： 介紹 傳統(tǒng)的輥筒破碎機(jī)因?yàn)榫哂袔讉€(gè)缺陷而導(dǎo)致了其在礦石處理應(yīng)用中的不受歡迎。尤其是當(dāng)與其它的一些破碎機(jī)比起來(lái)，諸如圓錐破碎機(jī)等，它們的低破碎比（一般局限在3以內(nèi)）和高的磨損率使它們沒(méi)有吸引力。然而，從礦石處理這一點(diǎn)來(lái)說(shuō)，輥筒破碎機(jī)有一些非常可取的特點(diǎn)：輥筒破碎機(jī)的相對(duì)穩(wěn)定的操作寬度可